Aluminum welding wire ER5356 (AlMg5)
Mark on AWS ER5356
Mark, GOST 7871-75
Description and characteristics:
Aluminum wire brand ER5356 widely zastosowania for welding profiles and structures of Al - Mg alloys containing 3% Mg, such as AMg3, AMg4, AMg5, AMg6 with the same. The shielding gas Ar / He. When the thickness 10mm or more the necessary heating to 150-200 ° C to reduce the probability of pore formation. Not recommended for thicknesses greater than 20 mm
Diameter, mm
Weight
MIG
0.8
2.0 kg
1.0
2.0 kg
1.0
7.0 kg
1.2
2.0 kg
1.2
7.0 kg
TIG
2.0
5.0 kg
2.4
5.0 kg
3.2
5.0 kg
Chemical composition of wire (%)
Si
Mg
Fe
Cu
Mn
Zn
Ti
Al
0.25
4.5-5.5
≤ 0.4
≤ 0.1
0.05-0.2
≤ 0.1
0.06-0.2
Rem
Mechanical properties of all weld metal (%)
Limit fluidity
δ 0.2(MPa)
Strength stretching,
δ b(MPa)
Elongation,
δ 5(%)
120
265
26
Advantages of brand products "CORAL":
Surface quality alumniCSOs wire is controlled at all stages of manufacture.
Aluminum wire brand ER5356 is continuously monitored in the production process for compliance the requirements of standards.To standards - homogeneity of the material throughout the length of the aluminum rod - guarantee the continuity of the welding process without splashing of the material, its foaming and boiling.
According to the standards of AWS A5.10 DIN 1735 and GOST 7871-75 in the composition of the material other than aluminium bases are not less than 4.5% magnesium. The wire surface is clean, no burrs, dents, bundles and traces of curves.
Package:
Aluminum wire brand ER5356 trademark "CORAL" is available in plastic cassettes. All the wire is wound tightly in a row (round to round).
Plastic cassettes Packed in plastic wrap and placed in a cardboard box with a unique design Company "CORAL".
To prevent moisture products each box with product supplied with celikoglu. Carton Packed on pallets.
Not recommended for thicknesses greater than 20 mm When thicknesses of 10 mm and more necessary heating to 150-200 ° C to reduce the probability of pore formation.