HTS-2000 Solder (solder) soldering aluminum

Scope:
Repair and reconditioning of cylinder heads (cracks, chips, burnouts, etc)
Repair aluminum fuel tanks
Repair of pipes and heat exchangers of air conditioners
Repair cracks and holes in the aluminum hull boats and boats
Restoring broken brackets from aluminum alloys and. so on Repairing aluminum housings, trays, enclosures and so on. Fusion seats bearings in aluminum products. The restoration of the screw holes.
Characteristics of the alloy HTS 2000:
• Bar diameter 2-3 mm Length 46 see
• Weight 1 rod 11-12 grams. (100 gr. - 8-9 PCs)
Color - silver
• Tensile strength - PSI 45,900
• Elongation of 10% in 2 inches
• Impact strength (Charpy) - 43 Ft. lbs
• Shear strength - 31,000 PSI
• Share - 6.6
• The melting temperature of 390°
• Linear coefficient of expansion - 15.2×10 - 6in./in./F°
• The electrical conductivity of 26% (STD. copper)
• Rockwell: 48
• Weight 0.24 lbs/inch3
DESCRIPTION USE SOLDER HTS-2000
Step 1: be SURE to clean the surface with a file, grinding stone or brushed stainless steel (remove oxide film).
Step 2: Heat the working surface (but not rod alloy HTS-2000) to a temperature close to 200 degrees and for better penetration of the solder if possible clean again (because when heated aluminum appears oxide film) then adjust the temperature of the metal (parts) up to the melting point of the solder ( 390° C). DO NOT PLACE THE ROD ALLOY HTS-2000 IN FLAMES. You must bring the surface temperature of the particular metal (parts) up to the melting point of the flux of the rod ( 390° C) alloy HTS-2000. Open structural pores of the working surface by using heat to penetrate deep into the metal alloy.
Step 3: Surface and thin threadlike aluminum will saladita, scratching her by the rod, when the appropriate temperature is reached. For all other cases, use ludilnoe brush stainless steel (you can use dental tools for tinning the surface using the rod alloy HTS-2000.
Step 4: Upon completion of the repair, allow material to cool naturally. Propane is better to apply for products up to 10mm. For larger sizes, use of acetylene.
Note: Remember, the thicker the material, the more time is needed to achieve the desired temperature. For heavier work or in order to reduce the time can use oxygen - acetylene or use an additional heating of the details of other sources of heat (stove, oven, blowtorch) Always use a special turbo nozzle or a neutral flame.
Payment to PrivatBank card or cod.
The mandrel Ukraine TC New mail.
The minimum number 3 rod.
Price up to 10pcs-35grn/piece
over 10-30/piece
For more information please contact us by phone, we will be glad to help You.